Title
Strengthening Mechanism of Complex Precipitation in Fe - Cu - Ni - Al Alloy
손유홍Y . H . Shon, 조현기H . K . Cho
Abstract
Detailed examination was carried out for clarifying the strengthening mechanism of complex precipitation during aging at 100∼600℃ in Fe-1Cu, Fe-3Ni-1Al and Fe-1Cu-3Ni-1Al alloys by the measurements of hardness, impact test, differential thermal analysis and the transmission electron micrography observation. Among the alloys studied Fe-1Cu-3Ni-1Al alloy aged at 500℃ showed the largest hardness increase with time while the impact energy value decreased concurrently. The phases precipitated in the ferrite matrix during aging at 500℃ were found to be ε-Cu and NiAl intermetallic compound. It was also observed that the ε-Cu coarsened rapidly and became randomly oriented large particles tending to be overawed whereas NiAl precipitates grew very slowly and kept coherency with the ferrite matrix showing no overaging for a considerable period of prolonged aging. It was concluded that the major strengthening mechanism during aging at 500℃ in Fe-1Cu-3Ni-1Al was the coherent precipitation of NiAl phase in ferrite matrix. The role of Cu in Fe-1Cu-3Ni-1Al was interpreted as the promotion of NiAl precipitation so that the alloy could reach its maximum hardness more rapidly.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.