Title
Behavior of Small Crack Growth in Steam Turbine Blade Material
남승훈Seung Hoon Nahm, 이주진Joo Jin Lee, 허용학Yong hak Huh, 전승범Seung Bum Joen, 이해무Hae Moo Lee
Abstract
In order to evaluate the life of steam turbine blade, information of the crack initiation at corrosion pits and the crack growth is needed. Corrosion pits are made artificially on the specimens machined from the real turbine blades(12% Cr steel) and specimens are tested to study the small crack initiation and growth. Difference between the small cracks and the long cracks is made by the crack growth behavior and the size of small cracks is 700∼800㎛ equivalent to 14∼18 times of grain size. The formation fife of these small cracks reveals 80∼90% of total fatigue life and those life with smaller applied stress shows larger portion of total life than that of larger stress.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.