Vol.48, No.7, 639 ~ 644, 2010
|
| Title |
| Rapid Sintering of FeAl by Pulsed Current Activated Heating and its Mechanical Properties |
| 손인진 In Jin Shon , 고인용 In Yong Ko , 윤진국 Jin Kook Yoon , 도정만 Jung Mann Doh , 조승훈 Seung Hoon Jo |
|
|
|
| Abstract |
| Nanopowder of FeAl was synthesized by high energy ball milling. Using the pulsed current activated sintering method, a dense nanostuctured FeAl was consolidated within 2 minutes from mechanically synthesized powders of FeAl and horizontally milled powders of Fe+Al. The grain size and hardness of FeAl sintered from horizontally milled Fe+Al powders and high energy ball milled FeAl powder were 150 nm, 50 nm and 466 kg/mm2, 574 kg/mm2, respectively. |
|
|
| Key Words |
| intermetallics, sintering, self-propagating synthesis, mechanical properties, X-ray diffraction |
|
|
 |
|