Vol.48, No.12, 1078 ~ 1084, 2010
|
| Title |
| High Temperature Oxidation Behavior and Mechanical Characteristic of Recrystallized Alloy 617 |
| 임정훈 Jeong Hun Lim , 조태선 Tae Sun Jo , 박지연 Ji Yeon Park , 김영도 Young Do Kim |
|
|
|
| Abstract |
| In this study, high temperature oxidation behavior of Alloy 617 was investigated to evaluate the effect of grain size for Alloy 617. The grain size of grain-refined Alloy 617 (GR617) was reduced to 5 μm from 71 μm for as-received Alloy 617 (AR617) by recrystallization after cold rolling. After high temperature aging, the oxide layers of AR617 and GR617 consisted of Cr2O3 external oxide scale and Al2O3 internal oxide. The external oxide scale resulted in a Cr-depleted zone and a carbide free zone below the scale. The depth of the carbide free zone was deeply formed in GR617. On the other hand, the depth of the internal oxide layer in GR617 was shorter than that in AR617. After a 3-point bending test, crack propagation of GR617 was more restricted than that of AR617 because of the different microstructure of the internal oxide. |
|
|
| Key Words |
| alloys, aging, grain refinement, carbide free zone, crack propagation |
|
|
 |
|