| Abstract |
| To investigate the relationship between heat treatment in zirconium alloy tubing process and metallurgical characteristics of Zr-1Nb-0.69Sn-0.11Fe alloy tubes, mechanical and oxidation behaviors of tubes heat treated at different temperatures after the final pilgering were investigated. The stress strain curves exhibited the saturation behaviors in all heat treatment conditions (460~600℃) in this study with the onset strain of saturation increased with increase of post-pilgering annealing temperature. The strength fell off rapidly with increasing annealing temperature. The ultimate strength of the low tin Zr-1Nb-0.69Sn-0.11Fe alloy with slightly higher iron and oxygen contents in this study was found to be higher than Zr-1Nb-1Sn- 0.1Fe alloy. The oxidation experiments in steam condition revealed that the corrosion resistance of low tin Zr-1Nb-0.69Sn-0.11Fe alloy was better than the Zr-1Nb-1Sn-0.1Fe alloy with a higher Sn content. The weight gain of low tin Zr-1Nb-0.69Sn-0.11Fe alloy tubes gradually increased with the increasing annealing temperature possibly due to the decreased Nb content in the matrix because of the formation of β-Nb particles. |
|
|
| Key Words |
| low tin, Zirlo, tension test, annealing, uniform strain |
|
|
 |
|