Mechanical Properties and Fabrication of Nanostructured (Ti,Mo)Si2 by Pulsed Current Activated Combustion |
고인용 In Yong Ko , 박나라 Na Ra Park , 오세훈 Se Hoon Oh , 손인진 In Jin Shon |
|
|
|
Abstract |
Nanopowders of Mo, Ti and Si were made by high-energy ball milling. A dense nanostructured (Ti,Mo)Si2 compound was sintered by the pulsed current activated combustion method within two minutes from mechanically activated powder of Mo, Ti and Si. A highly dense (Mo,Ti)Si2 compound was produced under simultaneous application of 80 MPa pressure and a pulsed current. The mechanical properties and micorostructure were investigated. The hardness and fracture toughness of the (Mo,Ti)Si2 were 1030 kg/mm2 and 4.9 MPa·m1/2, respectively. The mechanical properties were higher than monolithic TiSi2. |
|
|
Key Words |
compound, nanostructure, sintering, mechanical properties |
|
|
|
|