Vol.55, No.2, 91 ~ 98, 2017
|
| Title |
| Study on the Mechanical Properties and Corrosion Behaviors of Fe-(20, 45) wt% Gd Intermetallics |
| 강보경 Bo Kyeong Kang , 백열 Youl Baik , 최용 Yong Choi , 문병문 Byung Moon Moon |
|
|
|
| Abstract |
| Fe-(20, 45 wt%) Gd intermetallics were vacuum arc melted as the mother alloy of a neutron shielding and absorbing material. The structure of the cast Fe-20 wt% Gd intermetallics had primary dendrites with a short width of about 2 μm, which became coarse with increasing Gd content. The final compositions of the Fe-20 wt% Gd and Fe-45 wt% Gd intermetallics determined by Rietveld refinement were mainly Fe3Gd with 26.6 at% Fe2Gd, and Fe3Gd with various intermetallics like 13.9 at% Fe2Gd, 7.3 at% Fe9Gd and 3.9 at% Fe17Gd2, respectively. The micro-hardnesses, yield strength, ultimate compressive strength and elongation of the Fe-20 wt% Gd intermetallics were 629±12 Hv, 753 MPa, 785 MPa and 4%, respectively, and those of the Fe-45 wt% Gd intermetallics were 741±13 Hv, 772 MPa, 823 MPa and 3%. Passivity was not present in artificial sea water at room temperature. The corrosion potentials and the corrosion rates of the Fe-20 wt% Gd and Fe-45 wt% Gd intermetallics were -624 mVSHE, 2.771 mA/cm2, and -804 mVSHE, 3.397 mA/cm2, respectively. The corroded surface of the Fe-Gd intermetallics contained corrosion products like gadolinium with iron, which detached to leave a trail of pits. †(Received April 11, 2016; Accepted August 29, 2016) |
|
|
| Key Words |
| gadolinium, gd intermetallics, rietveld refinement, mechanical properties, corrosion behaviors |
|
|
 |
|