| Abstract |
| Spent electroplating solutions contain small amounts of Pd(II). Cementation of Pd(II) with zinc metal powder is practiced to concentrate the Pd. Dissolution of the cemented Pd metal is necessary to recover pure Pd metal or compounds. In this work, the leaching behavior of Pd metal in inorganic acid solutions (hydrochloric and sulfuric acid) in the presence of an oxidizing agent such as H2O2, NaClO3, or NaClO was investigated. To determine the optimum conditions for Pd leaching, experiments were conducted by adjusting the concentration of the acids and oxidizing agents, reaction temperature and time, and pulp density. Complete leaching of Pd was possible using a hydrochloric acid solution with 3 kinds of oxidizing agents, whereas only NaClO was effective in the leaching with sulfuric acid solution. The chloride ions of HCl and NaClO3/NaClO play an important role in enhancing the leaching of Pd, due to the formation of Pd chlorocomplexes and by decreasing the reduction potential of Pd(II). Compared to H2O2, NaClO3 and NaClO showed some merits as oxidizing agents in terms of reaction time, temperature and low acid concentration. Based on the optimum leaching conditions of single Pd metal, the conditions for the complete leaching of Pd and Zn from the metallic mixtures were obtained.
(Received March 24, 2021; Accepted April 26, 2021) |
|
|
| Key Words |
| leaching, inorganic acid, oxidizing agent, palladium, zinc |
|
|
 |
|